316/316L dual certified stainless sheet is an "18-8" austenitic chromium-nickel steel modified by the addition of molybdenum, which greatly increases the corrosion resistance as well as the mechanical properties at elevated temperatures. 316/316L is non-magnetic in the annealed condition and not hardenable by heat treatment. 316/316L is more resistant to atmospheric and general corrosive conditions than any of the other standard stainless steels. The addition of molybdenum provides an extra measure of corrosion resistance making this grade suitable for applications involving severe corrosive conditions such as use in the chemical industries and marine atmospheres. This grade of stainless may become slightly magnetic when cold worked. 316/316L is sheared to size or can be cut into shapes or rings on Speedy Metals High Definition Plasma cutter.

ANALYSIS

316/316L stainless sheet conforms to ASTM A167, ASTM A240, MIL-S-5089, QQ-S-766

MECHANICAL PROPERTIES

The above values are average and may be considered as representative of 316/316L stainless

APPLICATIONS

316/316L is used extensively for paper pulp handling equipment, process equipment for producing photographic chemicals, inks, rayon, rubber, textile bleaches and dyestuffs and high temperature equipment. Since 316/316L has good cold forming and drawing properties, it is an outstanding stainless steel for a large number of applications. Manufactured by the electri-furnace process, 316/316L meets the exacting standards of the aircraft industry. Widely used in the chemical industry. Used in the manufacture of pharmaceuticals in order to avoid excessive metallic contamination, medical instruments, food preparation equipment. Because 316/316L possesses the highest creep and tensile strengths at elevated temperatures of any of the more commonly used stainless steels, it finds extensive use where the combination of high strength and good corrosion resistance at elevated temperatures is required

MACHINEABILITY AND WELDABILITY

Machinability is rated at 36% of B1112. Average cutting speed 60 ft/min. Easily welded by all commercial processes except forge or hammer welding. Annealing is recommended after forging to maintain maximum corrosion resistance.
316/316L can be forged between 2100°-2300° F. Do not forge below 1700° F.

HEAT TREATING

316/316L is not hardenable by heat treatment. Cold working increases tensile strength and hardness. Annealing range is between 1850° and 2050°F. Cool rapidly. Water should be used for heavier sections; air for lighter sections. The stress relieving range is between 400° and 750°F.

TOLERANCES

Thickness - Inch Gage Number Tolerance*
.1875 to .14518 & 90.007
.1451 to .1301100.006
.1301 to .1141110.005
.1141 to .0981120.005
.0981 to .0831130.004
.0831 to .0721140.004
.0721 to .058115 & 16
.0581 to .040117 to 190.003
.0401 to .029120 to 220.002
.0291 to .016023 to 270.0015

* up to 48" wide, mill produced

SPEEDY METALS ITEMS

20ga (.036") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis 18ga (.048") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis 16ga (.060") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis
14ga (.075") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis 13ga (.090") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis 12ga (.105") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis
11ga (.120") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis 10ga (.135") 316 Stainless Steel, Cold Rolled & Annealed, 2B Finis